To evaluate the rate of thermal embrittlement of type 316 low-carbon stainless steel weld metal at BWR operating temperature, aging test at 310°C, 335°C, and 400°C was carried out. Hardness of each ferrite and austenite phase of s pecimens was measured selectively by microhardness tester. Hardness of ferrite was increased apparently with all three aging temperatures, whereas hardness of austenite was not changed. Changes in the microstructure of ferrite ag ed at 310°C for 11,000h and 18,000h were analyzed ...
英字タイトル:
Evaluation of aging embrittlement of low-carbon austenitic stainless steelweld metal near the BWR operating temperature